Fecral resistohm145 A1 Kan- Thal D A1 Tk1 Kan A1 APM Uaea vevela vevela maualuga
TK-APMFerro-Chromium-Aluminum Alumea
O lenei oloa e fa'aaogaina matai u'amea e pei o mea mata, fa'aogametallurgy pautatekinolosi
e gaosia ingots u'amea, ma e gaosia e faapitoa malulu ma vevela faagasologa ma vevela
faiga togafitiga. O le oloa o loʻo i ai le lelei o le malosi faʻamaʻi faʻamaʻi, lelei
tete'e corrosion i le vevela maualuga, fetolofi laiti o vaega electrothermal, auaunaga umi
ola i le vevela maualuga ma suiga laiti o le tetee. E fetaui mo le maualuga o le vevela 1420 C,
maualuga le malosi density, corrosive atemosifia, siosiomaga carbon ma isi siosiomaga galue.
E mafai ona faʻaaogaina i ogaumu sima, ogaumu vevela vevela vevela, ogaumu suʻesuʻe,
ogaumu tau alamanuia faaeletonika ma ogaumu faasalalau.
(Wt%）fatuga autu
|
| C | Si | Mn | Cr | Al | Fe |
| Min | - | - | - | 20 | 5.5 | Bal. |
| Max | 0.04 | 0.5 | 0.4 | 22 | 6.0 | Bal. |
Mea fa'ainisinia autu
Malosi Tensile i le vevela o le potu: 650-750MPa
Fa'atelega fua faatatau: 15-25%
maaa: HV220-260
1000℃Malosi o le Tensile ile 1000 ℃ Temperature 22-27MPa
1000℃6MPaTempera maualugaDurability i le 1000 Temperature ma 6MPa ≥100h
O mea totino autu
mafiafia 7.1g/cm3
resistivity 1.45×10-6 Ω.m
Tete'e Temperature Coefficient(Ct）
| 800 ℃ | 1000℃ | 1400 ℃ |
| 1.03 | 1.04 | 1.05 |
Fuafuaga fa'alautele laina laina(）
| 20-800 ℃ | 20-1000 ℃ | 20-1400 ℃ |
| 14 | 15 | 16 |
mea liusuavai：1500℃Maualuluga Fa'aauauina Galulue vevela 1400 ℃
Olaga vave
|
| 1300℃ | 1350 ℃ |
|
Ole ola vave (itula)
| 110 | 90 |
|
Fa'ase'e fua ina ua malepe
| 8 | 11 |
Suʻega e tusa ai ma le GB / T13300-91 auala masani
Fa'amatalaga
Uea lautele lautele:φ0.1-8.5mm
mafiafia uaea lipine:0.1-0.4mm; lautele: 0.5-4.5mm
Lipine mafiafia mafiafia:0.5-2.5mm; lautele: 5-48mm