Fa'afeiloa'i i la matou upega tafa'ilagi!
ASTM TM2 Bimetal Ribbon Fa'aaogaina mo le Pulea Faiga
O le uiga autu o le bimetal vevela o loʻo suia ma le vevela ma le vevela deformation, e mafua ai se taimi faapitoa. Tele masini faʻaaogaina lenei vaega e faʻaliliu ai le malosi o le vevela i galuega faʻainisinia e ausia ai le pulea otometi. Thermal bimetal faʻaaogaina mo le faʻaogaina o le masini ma le vevela vevela i le fuaina. meafaigaluega.
| fa'ailoga faleoloa | 5j1480 | |
| Fa'atasi ma fa'ailoga | 5j18 | |
| Papa tu'ufa'atasi fa'ameamea | Fa'alautelega maualuga | Ni22Cr3 |
| vaega ogatotonu | ——– | |
| La'ei fa'alautele maualalo | Ni36 | |
Fa'ameamea
| fa'ailoga faleoloa | Ni | Cr | Fe | Co | Cu | Zn | Mn | Si | C | S | P |
| ≤ | |||||||||||
| Ni36 | 35.0~37.0 | - | alauni | - | - | - | ≤0.6 | ≤0.3 | 0.05 | 0.02 | 0.02 |
| Ni22Cr3 | 21.0~23.0 | 2.0~4.0 | alauni | - | - | - | 0.3~0.6 | 0.15~0.3 | 0.25~0.35 | 0.02 | 0.02 |
faatinoga
| Nai lo le punou K(20~135ºC) | Curvature vevela F/(falematamata ~ 130 ºC) | teteega | Linear vevela /ºC | Fa'ataga le fa'aogaina o le vevela / ºC | Malosi (g/cm pe a uma) | |||
| Numera tau | Se'ese'ese faatagaina | Tulaga taua | Se'ese'ese faatagaina | |||||
| Laasaga 1 | Laasaga 2 | |||||||
| 14.3 | ±5% | ±7% | 26.2%±5% | 0.8 | ±5% | -20~180 | -70~350 | 8.2 |
| Modulus o elasticity E/GPa | Malosi (HV) | Malosi fa'asa MPa | Fa'ataga le mamafa MPa | ||
| Fa'alautelega maualuga | La'ei fa'alautele maualalo | aupito maualalo | tele | ||
| 147–177 | 270~340 | 200~255 | 785~883 | 196 | 343 |
Tusi lau savali iinei ma lafo mai ia i matou