FeCrAl A1 APM AF D Alloy uaea eletise e tetee i le vevela
Fa'amatalaga tele
| Igoa o oloa | Tele tele |
| Uaea tusi malulu | Diamita 0.03-7.5mm |
| Uaea uaea vevela | Diamita 8.0-12mm |
| lipine | Mafiafia 0.05-0.35mm |
| Lautele 0.5.0-3.5mm | |
| Fa'ailoga taai malulu | Mafiafia 0.5-2.5mm |
| Lautele 5.0-40mm | |
| fasimea taai vevela | Mafiafia 4-6mm |
| Lautele 15-40mm |
vaega faavae:
| fa'avae fa'avae | APMTM | FeCrAl | ||
| A-1 | AF | D | ||
| Le maualuga o le vevela galue faifai pea | 1425 | 1400 | 1300 | 1300 |
| Ole igoa ole vaila'au,% Cr | 22 | 22 | 22 | 22 |
| AI | 5.8 | 5.8 | 5.3 | 4.8 |
| Fe | mea aoga | mea aoga | mea aoga | mea aoga |
| Ni | - | - | - | - |
| Le resistivity i le 20ºC,Ωmm-2mm-1 | 1.45 | 1.45 | 1.39 | 1.35 |
| mafiafia,g/cm3 | 7.1 | 7.1 | 7.15 | 7.25 |
| Fa'alili fa'aalili fa'avelaK-1 20-750ºC | 14×10-6 | 14×10-6 | 14×10-6 | 14×10-6 |
| 20-1000ºC | 15×10-6 | 15×10-6 | 15×10-6 | 15×10-6 |
| Le fa'avevela vevela 20ºC,Wm-1K-1 | 13 | 13 | 13 | 13 |
| Malosiaga vevela fa'apitoa 20ºC,KJkg-1K-1 | 0.46 | 0.46 | 0.46 | 0.46 |
| Liu liusua°C | 1500 | 1500 | 1500 | 1500 |
| Masalo o uiga faʻainisinia | ||||
| Malosi tete,N mm-2 | 680 | 680 | 680 | 650 |
| Le malosi e maua ai, N mm-2 | 470 | 475 | 475 | 450 |
| Malosi,Hv | 230 | 230 | 230 | 230 |
| Fa'aliga fa'aumi,% | 20 | 18 | 18 | 18 |
| 900ºCT malosi,N mm-2 | 40 | 34 | 37 | 34 |
| Malosi fetolofi 800ºC | 11 | 6 | 8 | 6 |
| 1000ºC | 3.4 | 1 | 1.5 | 1 |
| Maneta | maneta(I le vevela600ºC) | |||
| Emissivity, tulaga oxidation | 0.7 | 0.7 | 0.7 | 0.7 |