E uiga i le Uaea Fa'avevela Tete'e:
O matou o le kamupani gaosi oloa sili ona lelei i le gaosiga o le u'amea fa'avevela tete'e i Saina, fa'apitoa i le uaea Ferro-Chrome (Fe-Cr-AL), uaea Nickel-Chrome (Nichrome), uaea Copper Nickel (Constantan), uaea u'amea e le gaoia ma oloa fa'atatau i u'amea fa'afefiloi ua fa'atulagaina e fa'afetaui ai mana'oga fa'apitoa a tagata fa'atau.

Fa'amatalaga o le tele

fa'atulagaga fa'avae:

fa'atulagaga fa'avae	Kanthall APMTM	Kanthall
		A-1	AF	D
Le vevela sili ona maualuga o le galue faifai pea	1425	1400	1300	1300
O le tuufaatasiga fa'akemikolo masani,% Cr	22	22	22	22
AI	5.8	5.8	5.3	4.8
Fe	mea fa'aoga	mea fa'aoga	mea fa'aoga	mea fa'aoga
Ni	-	-	-	-
O le tete'e i le 20ºC,Ωmm-2mm-1	1.45	1.45	1.39	1.35
mafiafia,g/cm3	7.1	7.1	7.15	7.25
Fa'asologa o le fa'alauteleina o le vevela K-1 20-750ºC	14×10-6	14×10-6	14×10-6	14×10-6
20-1000ºC	15×10-6	15×10-6	15×10-6	15×10-6
O le fa'avevela o le 20ºC,Wm-1K-1	13	13	13	13
Malosiaga fa'apitoa o le vevela 20ºC,KJkg-1K-1	0.46	0.46	0.46	0.46
Tulaga e liusuavai aiºC	1500	1500	1500	1500
Atonu o uiga fa'amekanika
Malosiaga o le tensile, N mm-2	680	680	680	650
O le malosi e maua mai ai, N mm-2	470	475	475	450
Ma'a'a, Hv	230	230	230	230
Fa'alēgaina o le fa'alēga,%	20	18	18	18
900ºCTmalosi malosi,N mm-2	40	34	37	34
Malosi totolo 800ºC	11	6	8	6
1000ºC	3.4	1	1.5	1
Maneta	maneta (I le vevela 600ºC)
Emissivity, o tulaga o le oxidation	0.7	0.7	0.7	0.7

Fa'amatalaga:

Ituaiga o le Alloy	Lapo'a	Tete'e	Fa'agaoioi	Fa'aloloa (%)	Punou	Fa'aauau pea	Olaga Faigaluega
	(mm)	(μΩm)(20°C)	Malosi		Taimi	Auaunaga	(itula)
			(N/mm²)			Vevela (°C)
Cr20Ni80	<0.50	1.09±0.05	850-950	>20	>9	1200	>20000
	0.50-3.0	1.13±0.05	850-950	>20	>9	1200	>20000
	>3.0	1.14±0.05	850-950	>20	>9	1200	>20000
Cr30Ni70	<0.50	1.18±0.05	850-950	>20	>9	1250	>20000
	≥0.50	1.20±0.05	850-950	>20	>9	1250	>20000
Cr15Ni60	<0.50	1.12±0.05	850-950	>20	>9	1125	>20000
	≥0.50	1.15±0.05	850-950	>20	>9	1125	>20000
Cr20Ni35	<0.50	1.04±0.05	850-950	>20	>9	1100	>18000
	≥0.50	1.06±0.05	850-950	>20	>9	1100	>18000
1Cr13Al4	0.03-12.0	1.25±0.08	588-735	>16	>6	950	>10000
0Cr15Al5		1.25±0.08	588-735	>16	>6	1000	>10000
0Cr25Al5		1.42±0.07	634-784	>12	>5	1300	>8000
0Cr23Al5		1.35±0.06	634-784	>12	>5	1250	>8000
0Cr21Al6		1.42±0.07	634-784	>12	>5	1300	>8000
1Cr20Al3		1.23±0.06	634-784	>12	>5	1100	>8000
0Cr21Al6Nb		1.45±0.07	634-784	>12	>5	1350	>8000
0Cr27Al7Mo2	0.03-12.0	1.53±0.07	686-784	>12	>5	1400	>8000

Tulaga lelei:
E maualuga ma mautu le tete'e atu o le u'amea fa'a-nickelchromium, e tete'e atu i le 'ele, e lelei le tete'e atu i le fa'a'ele'eleina o luga, e sili atu le malosi i le vevela maualuga ma le mafui'e, e lelei le ductility, e faigofie ona galue ma e mafai ona fa'apipi'i.