Nichrome / Elemene VevelaUaea tetee/ Uaea Mafolafola
Ni80Cr20o se nickel-chromium alloy (NiCr alloy) o loʻo faʻaalia i le maualuga o le resistivity, lelei le faʻamaʻiina o le faʻamaʻiina ma le lelei tele o le mautu.E fetaui lelei mo le faʻaaogaina i le vevela e oʻo atu i le 1200 ° C, ma umia se olaga sili atu le tautua pe a faʻatusatusa i le uʻamea chromium alumium.
Talosaga masani moNi80Cr20o elemene faʻavevela eletise i mea faʻaoga fale, ogaumu faʻapisinisi ma faʻalavelave (tetee uaea, faʻamaʻi ata tifaga), uʻamea mafolafola, masini auli, faʻavevela vai, paʻu palasitika paʻu, uʻamea faʻapipiʻi, elemene tubular sheathed uʻamea ma elemene kalama.
Tulaga masani%
C | P | S | Mn | Si | Cr | Ni | Al | Fe | Isi |
Max | |||||||||
0.03 | 0.02 | 0.015 | 0.60 | 0.75~1.60 | 20.0~23.0 | Bal. | Max 0.50 | Max 1.0 | - |
Mea fa'ainisinia masani(1.0mm)
Tuuina atu le malosi | Malosi Tetele | Fa'aumiumi |
Mpa | Mpa | % |
420 | 810 | 30 |
Meatotino Faaletino masani
Malosi (g/cm3) | 8.4 |
Tete'e eletise ile 20ºC(mm2/m) | 1.09 |
Coefficient conductivity ile 20ºC (WmK) | 15 |
Coefficient o le faalauteleina o le vevela | |
vevela | Coefficient o le fa'alauteleina o le vevela x10-6/ºC |
20ºC-1000ºC | 18 |
Maoti le malosi o le vevela | |
vevela | 20ºC |
J/gK | 0.46 |
Mea liusuavai (ºC) | 1400 |
Max fa'aauauina pea le vevela ile ea (ºC) | 1200 |
Mea fa'amaneta | e le fa'amaneta |
Temperature Factors O le Resistivity Faaeletise | |||||
20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 600ºC |
1 | 1.006 | 1.012 | 1.018 | 1.025 | 1.018 |
700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1300ºC |
1.01 | 1.008 | 1.01 | 1.014 | 1.021 | - |
Sitaili o sapalai
Igoa Alloys | Ituaiga | Fua | ||
Ni80Cr20W | Uaea | D=0.03mm~8mm | ||
Ni80Cr20R | lipine | W=0.4~40 | T=0.03~2.9mm | |
Ni80Cr20S | Aveese | W=8~250mm | T=0.1~3.0 | |
Ni80Cr20F | Iila | W=6~120mm | T=0.003~0.1 | |
Ni80Cr20B | Pa | Dia=8~100mm | L=50~1000 |