Alkrothal 14 ferritic ironchromiumuminium alloy (FeCrAl alloy)
Alkrothal 14 (Resistance heat wire ma resistance wire) Alkrothal 14 o se ferritic ironchromiumuminium alloy (FeCrAl alloy) faʻatasi ai ma le maualuga o le resistivity talafeagai mo le faʻaogaina i le vevela e oʻo atu i le 1100°C (2010°F).Alkrothal 14 e masani ona faʻaaogaina mo uaea faʻafefe eletise mo faʻaoga e pei o uaea faʻamafanafana.
FA'AIGA KEMIMI
| C % | Si % | Mn % | Cr % | Al % | Fe % | |||||||
| fa'ailoga igoa | 4.3 | Bal | ||||||||||
| Min | - | 14.0 | ||||||||||
| Max | 0.08 | 0.7 | 0.5 | 16.0 |
MESINIA MESINIA
| tele uaea | Tuuina atu le malosi | Malosi fa'asa | Fa'aumiumi | Malosi |
| Ø | Rp0.2 | Rm | A | |
| mm | MPa | MPa | % | Hv |
| 1.0 | 455 | 630 | 22 | 220 |
| 4.0 | 445 | 600 | 22 | 220 |
| 6.0 | 425 | 580 | 23 | 220 |
MODULUS A TALAVOU
| vevela °C | 20 | 100 | 200 | 400 | 600 | 800 | 1000 |
| GPa | 220 | 210 | 205 | 190 | 170 | 150 | 130 |
Mea tau masini i le maualuga o le vevela
| Vevela °C | 900 |
| MPa | 30 |
Ole fua ole suiga ole malosi ole malosi ole 6.2 x 10/min
MALOSI MOTOGO - 1% FA'ATA'U I LE 1000 H
| Vevela °C | 800 | 1000 |
| MPa | 1.2 | 0.5 |
METOTIA FAALETINO
| Malosi g/cm3 | 7.28 |
| Tete'e eletise ile 20°C Ω mm/m | 1.25 |
| fua faatatau a Poisson | 0.30 |
FA'ATA'U O LE MAUA O LE TETEE
| Tempera°C | 100 | 200 | 300 | 400 | 500 | 600 | 700 | 800 | 900 | 1000 | 1100 |
| Ct | 1.00 | 1.02 | 1.03 | 1.04 | 1.05 | 1.08 | 1.09 | 1.10 | 1.11 | 1.11 | 1.12 |
COEFFICIENT O LE FA'ALUA'E LE MAUA
| Vevela °C | Fa'ateleina le vevela x 106/ K |
| 20 - 250 | 11 |
| 20 - 500 | 12 |
| 20 - 750 | 14 |
| 20 - 1000 | 15 |
FA'AMALELE
| Vevela °C | 20 |
| W/m K | 16 |
FA'ATOA'OGA FA'AVAE FA'AVAE
| Tempera°C | 20 | 200 | 400 | 600 | 800 | 1000 |
| kJ kg-1K-1 | 0.46 | 0.63 | 0.72 | 1.00 | 0.80 | 0.73 |